Brazing Flux FAQs
Straight answers to the questions people ask most when choosing and using brazing and soldering flux.
How do I choose the right flux?
Choose the flux to match the filler metal, the metals being joined and the temperature you will work at. Fluxes are made for particular jobs: silver brazing, bronze brazing, aluminium, stainless steel and soft soldering each have their own types, and they are not interchangeable.
The filler maker normally says which flux to use with a given rod. Check the pack for the metals it is intended for and for its working temperature range, and make sure it covers the temperature at which your filler melts and flows.
Do I need flux for every brazing job?
Most brazing needs flux, but some filler metals are self-fluxing in certain uses. For example, copper-phosphorus rods can be used without flux when joining copper to copper, because the phosphorus does the job. They still need flux on brass and bronze, and they are not suitable for joining steel.
Some aluminium fillers carry flux in the core. Always check the instructions for the rod you are using, and use flux where there is any doubt.
How do I know when the joint is hot enough to add the filler?
Watch the flux. As the joint heats, most brazing fluxes bubble, dry out and turn into a clear, watery liquid when they reach working temperature. That is the signal that the metal is ready for the filler.
Heat the parent metal, not the rod, and let the heat from the joint melt the filler as you touch it on. If the filler does not flow, the joint is probably not hot enough, or the surface is not clean.
Do I still have to clean the metal before using flux?
Yes. Flux deals with the thin oxide film that forms on clean metal as it heats, but it cannot cope with oil, grease, paint, thick rust or dirt. Those need to be removed first by degreasing, and by brushing or abrading the surface until it is bright.
A clean, close-fitting joint plus the right flux gives the best chance of a strong, neat result. Many failed joints come from poor cleaning rather than from the flux or filler.